+++ oxides_system [2013/02/27 09:09] (current) – boltje
@@ Line 40: / Line 40: @@
     - Clean with IPA. This step is crucial!
   - Mount the sample with ''SPI silver paste plus II'' (should be kept in freezer, warm up before use) and squeeze the substrate against the heater with the glass tool (clean before use)
-  - Shine a halogene lamp on the substrate for 15 minutes
   - Cut away glue around the substrate
   - Mount side plates, push them flush against the substrate using a cotton tip.
@@ Line 90: / Line 89: @@
   - You will see that the conditioning of the target takes quite a while, check that while conditioning the voltage goes down to about the previous value in the logbook.
   - Presputter for >1 hour
-  - Program the heater in the meanwhile. There is a recipe for YBCO.
+  - Program the heater in the meanwhile.
 == Sputtering ==
@@ Line 114: / Line 113: @@
 ^ Material ^  Date     ^ Sample ID ^ Process parameters           ^ Measured with  ^ Result ^ Rate          ^
-|  LCMO    | 20060918  |   L408    |   3 mbar, 350mA ,384V                   |     X-ray       |  45 nm  |   1.21 nm/min   |
+|  LCMO    | 20060918  |   L408    |   3 mbar, 350mA ,384V                   |     X-ray       |  45 nm    | 1.21  nm/min   |
-|  Pt      | 20120711  |   Pt-01   |   1 mbar, 35mA, 603V, 19W, 15min        |     X-ray       |  11.5 nm  |   0.766 nm/min   |
+|  Pt      | 20120711  |   Pt-01   |   1 mbar, 35mA, 603V, 19W, 15min        |     X-ray       |  11.5 nm  | 0.766 nm/min   |
+|  LAO     | 20121210  | from Ishrad | DC 0.8 mbar, 30W                      |                 |           | ~0.18 nm/min   |
+====== Tech stuff ======
+  * Targets: 2 inch OD, 0.125 inch thick
+  * Backingcup: 53mm OD, 6.3mm thick